Processing Aid for Clear & Pigmented Polyolefinic Film

Description :
P-91010 PA is manufactured by compounding linear low density polyethylene with additives like antioxidant & special processing aids to improve the process ability. The masterbatch when added in small proportion say upto 1% to natural or pigmented polyolefins during film extrusion shows excellent processing performance during film manufacture.

Special Characteristics :
The additive even at low level of addition exhibits the following modification immediately after addition or after running for some time. 

  • Improves Flow Behaviour
  • Improves Productivity
  • Improves Gloss
  • Reduces Power Cost   
  • Reduces Die Pressure
  • Reduces Die build up
  • Reduces/ Eliminates Melt Fracture
  • Reduces Moisture Carrying

Technical Characteristics :

Physical Properties

Test Method

Unit

Typical Value

Specific Gravity

ASTM-D- 792

g/cc

0.93

Melt Flow Rate 190 ᵒC, 2.16 kg

ASTM–D-1238

g/10min.

1.80

Moisture Content

PPIL

PPM

< 600

Active Content

TGA

%

10

Color

Visual

-

Natural

Pre-drying: The Compound should be dried 70 ᵒC for 1 hr to its use.

Storage : The material shall be kept in a cool dry place for best results.

Form : The material is supplied in the form of Pellets.

Packing: HDPE/PP Woven Sack Bags of 25 kg.

We believe this information is based on the best currently available data on this subject.  It is offered as a possible helpful suggestion in experimentation you may care to undertake along these lines.  It is subjected to revision as additional knowledge and experience are gained.  PPIL makes no guaranttee to results and assumes no obligation or liability whatsoever in connection with this information.  This publication is not a license to operate under or intended to suggest infringement of any existing patents.